SURFACE MECHANISM OF CH4 REFORMING AND OXIDATION OVER NI *********************************************************************** **** * **** CH4 ON Ni - tested on MDR, MSR, CPOX * **** * **** Version 3.0 2014 * **** * **** K. Herrera Delgado, L. Maier, O. Deutschmann * **** KIT Karlsruhe * **** temp. range 500 - 2000K * **** * **** * **** Kinetic data format: DETCHEM * **** k = A * T**b * exp (-Ea/RT) A b Ea * **** (cm,mol,s) - kJ/mol * **** * **** STICK: A in next reaction is initial sticking coefficient * **** * **** $.. : additional coverage dependence of Ea (3rd column) * **** or changed reaction order (2nd column) * **** * **** see manuals on www.detchem.com for details * **** Surface site density: 2.66E-9 mol/cm**2 * **** * *********************************************************************** STICK (Ni) +(Ni) +H2 >H(Ni) +H(Ni) * 3.000E-02 -0.000 5.000 H(Ni) +H(Ni) >(Ni) +(Ni) +H2 * 2.544E+20 0.000 95.209 STICK O2 +(Ni) +(Ni) >O(Ni) +O(Ni) * 4.358E-02 -0.206 1.511 O(Ni) +O(Ni) >O2 +(Ni) +(Ni) * 1.188E+21 0.823 468.907 STICK (Ni) +CH4 >CH4(Ni) * 8.000E-03 0.000 -0.000 CH4(Ni) >(Ni) +CH4 * 8.705E+15 -0.000 37.550 STICK (Ni) +H2O >H2O(Ni) * 9.999E-02 0.000 -0.000 H2O(Ni) >(Ni) +H2O * 3.734E+12 -0.000 60.791 STICK (Ni) +CO2 >CO2(Ni) * 7.001E-06 -0.000 0.000 CO2(Ni) >(Ni) +CO2 * 6.442E+07 0.000 25.979 STICK (Ni) +CO >CO(Ni) * 4.999E-01 0.000 -0.000 CO(Ni) >(Ni) +CO * 3.566E+11 -0.000 111.271 $CO(Ni) 0.000 50.000 H(Ni) +O(Ni) >(Ni) +OH(Ni) * 3.951E+23 -0.188 104.346 (Ni) +OH(Ni) >H(Ni) +O(Ni) * 2.254E+20 0.188 29.644 H(Ni) +OH(Ni) >(Ni) +H2O(Ni) * 1.854E+20 0.086 41.517 (Ni) +H2O(Ni) >H(Ni) +OH(Ni) * 3.674E+21 -0.086 92.943 OH(Ni) +OH(Ni) >H2O(Ni) +O(Ni) * 2.346E+20 0.274 92.366 H2O(Ni) +O(Ni) >OH(Ni) +OH(Ni) * 8.148E+24 -0.274 218.494 C(Ni) +O(Ni) >(Ni) +CO(Ni) * 3.402E+23 -0.000 148.001 (Ni) +CO(Ni) >C(Ni) +O(Ni) * 1.758E+13 0.000 116.239 $CO(Ni) 0.000 50.000 CO(Ni) +O(Ni) >(Ni) +CO2(Ni) * 2.002E+19 -0.000 123.601 $CO(Ni) 0.000 50.000 (Ni) +CO2(Ni) >CO(Ni) +O(Ni) * 4.648E+23 -1.000 89.319 (Ni) +HCO(Ni) >H(Ni) +CO(Ni) * 3.710E+21 -0.000 0.003 $CO(Ni) 0.000 -50.000 H(Ni) +CO(Ni) >(Ni) +HCO(Ni) * 4.009E+20 -1.000 132.227 (Ni) +HCO(Ni) >CH(Ni) +O(Ni) * 3.796E+14 -0.000 81.911 CH(Ni) +O(Ni) >(Ni) +HCO(Ni) * 4.599E+20 0.000 109.969 (Ni) +CH4(Ni) >H(Ni) +CH3(Ni) 1.548E+21 0.087 55.825 H(Ni) +CH3(Ni) >(Ni) +CH4(Ni) 1.443E+22 -0.087 63.455 CH3(Ni) +(Ni) >H(Ni) +CH2(Ni) 1.548E+24 0.087 98.125 H(Ni) +CH2(Ni) >CH3(Ni) +(Ni) 3.091E+23 -0.087 57.205 (Ni) +CH2(Ni) >CH(Ni) +H(Ni) 1.548E+24 0.087 95.225 CH(Ni) +H(Ni) >(Ni) +CH2(Ni) 9.774E+24 -0.087 81.055 CH(Ni) +(Ni) >H(Ni) +C(Ni) * 9.888E+20 0.500 21.991 H(Ni) +C(Ni) >CH(Ni) +(Ni) * 1.707E+24 -0.500 157.919 CH4(Ni) +O(Ni) >CH3(Ni) +OH(Ni) 5.621E+24 -0.101 87.872 CH3(Ni) +OH(Ni) >CH4(Ni) +O(Ni) 2.987E+22 0.101 25.798 CH3(Ni) +O(Ni) >CH2(Ni) +OH(Ni) 1.223E+25 -0.101 130.672 CH2(Ni) +OH(Ni) >CH3(Ni) +O(Ni) 1.393E+21 0.101 19.048 CH2(Ni) +O(Ni) >CH(Ni) +OH(Ni) 1.223E+25 -0.101 131.372 CH(Ni) +OH(Ni) >CH2(Ni) +O(Ni) 4.407E+22 0.101 42.498 CH(Ni) +O(Ni) >C(Ni) +OH(Ni) * 2.471E+21 0.312 57.742 C(Ni) +OH(Ni) >CH(Ni) +O(Ni) * 2.433E+21 -0.312 118.968 CO(Ni) +CO(Ni) >CO2(Ni) +C(Ni) * 1.624E+14 0.500 241.761 $CO(Ni) 0.000 100.000 CO2(Ni) +C(Ni) >CO(Ni) +CO(Ni) * 7.294E+28 -0.500 239.239 (Ni) +COOH(Ni)>H(Ni) +CO2(Ni) 3.737E+20 0.475 33.656 H(Ni) +CO2(Ni) >(Ni) +COOH(Ni) 6.250E+24 -0.475 117.344 (Ni) +COOH(Ni)>CO(Ni) +OH(Ni) 1.461E+24 -0.213 54.366 CO(Ni) +OH(Ni) >(Ni) +COOH(Ni) 6.003E+20 0.213 97.634 $CO(Ni) 0.000 50.000 C(Ni) +OH(Ni) >H(Ni) +CO(Ni) * 3.888E+25 0.188 62.555 H(Ni) +CO(Ni) >C(Ni) +OH(Ni) * 3.522E+18 -0.188 105.495 $CO(Ni) 0.000 50.000 H(Ni) +COOH(Ni)>HCO(Ni) +OH(Ni) 6.000E+22 -1.163 104.878 HCO(Ni) +OH(Ni) >H(Ni) +COOH(Ni) 2.282E+20 0.263 15.922 END